Mak Premix Superior is an instant road repair compound which is manufactured with a blend of bitumen, aggregates and high grade polymers to ensure immediate bonding with existing surface. Repair of heavily trafficked road and airfield pavements using conventional materials and procedures is difficult, inconvenient to user and generally not very satisfactory. For such locations, ready to use patching materials to up- keep pavement traffic worthy, are essential.
Mak Premix Superior is specialised road patching product with high bitumen content >8% specially designed for long life and flexibility.
Mak Envirocool is nano insulation technology infused micro fiber reinforce waterproofing coating system. It is single component liquid applied flexible water & ultra violet resistance waterproofing membrane suitable for all types of expose roof, slab, terrace etc. It helps in reduction of energy usages by less heat transfer into buildings thus keeps the interiors cool. The coating serves the dual purpose of thermal reduction & with additional waterproofing protection. The excellent crack bridging property of Mak Envirocool revenge water leakages detect cause due to hair line cracks develop on the roof surfaces. This multipurpose product serves as waterproofing coating system with thermal reduction property which results in extended roofs/terrace/water tanks life.
Mak Elastothane EMB is a liquid applied polyurethane modified bituminous elastomeric membrane coating. Mak Elastothane EMB when applied on a surface, gives a continuous monolithic film which is rubbery and elastic in nature. The film is self-curing and cures by reaction with atmospheric moisture to give a tough elastomeric waterproof membrane.
Mak Elastothane EMB has good adhesion to a wide range of substrates such as concrete, brick, wood, slates, tiles, glass and metals etc. This is supplied also as a medium grade for roller, squeegee or brush application to horizontal as well as vertical surface.
Area of Application:
The high elasticity, excellent bond strength with concrete and other substrates, low water permeability of Mak Elastothane EMB makes it ideal membrane coating for a wide range of water / vapour proofing applications such as.
Foundations, Basements, Lift pits. Car decks, Podiums. Roof, terraces, Balconies, Patios. Sewage works and Sunken Portions.
The excellent chemical resistance of Mak Elastothane EMB is used as a barrier coating for any part of the external or internal faces of the structures where high degree of waterproofing is required.
1. Clean the surface thoroughly with wire brush, remove all dust, dirt, foreign Particles, fungi, etc. 2. Allow surface to be completely dry. Do not apply Mak Elastothane EMB on damp surface. 3. All the cracks/voids shall be sealed with rubberized Mak Sealing Compound (ISI) 4. Apply Mak Elastothane Primer @ 8-10 Sqm/l on the entire surface to be treated. Alternatively, dilute Mak Elastothane EMB in the ratio of 1:1 with either Xylene or Toluene. Allow the primer to dry. 5. Apply Mak Elastothane EMB by brush or spray @ 1 kg/sqm on the entire surface and upto 300 mm high on parapet wall. Allow it to dry. 6. Apply second coat of Mak Elastothane EMB @ 1 kg/sqm to achieve total dry film thickness of 1.5mm. 7. Reinforcement of Non-woven Polyester or Glass fiber of 40gsm may be provided between the layers for improved tensile strength. 8. Wearing course should done within 7 days.
Mak Elastothane PU Primer: 8-10 Sqm/l. Mak Elastothane EMB: 1.2 kg/Sqm on a smooth surface will provide an adequate. film thickness of approx. 1 mm. *Coverage rates may vary with surface texture and porosity.
Store in cool and dry place. Lid of the container should be properly closed after use. In very cold conditions store inside. Do not attempt to thin. Once opened Mak Elastothane EMB will start to cure and a skin will form, even in the resealed cans. This can be removed if material is used within approximately one month.
Health and Safety:
Keep away from sources of ignition Do not breathe vapour/spray Ensure good ventilation during application and drying In case of eye contact-wash with plenty of clean water and seek medical advice. Avoid prolonged skin contact wear suitable protective clothing and gloves while handling/applying. Remove from skin with mild solvent/hand cleanser and wash with warm soapy water.
A Joint Sealing Compound must display good adhesion towards concrete and has the ability to withstand extension without cracking. It must also have a low susceptibility to flow during hot weather conditions.
It should be durable and plastic, and at the same time offer resistance to ingress of solid foreign matter.
The Joint Sealing Compound is heated to temperature which will permit easy pouring into the expansion joint above the joint filler. This temperature should be well below that at which Joint Sealing Compound undergoes decomposition and should not exceed temperature as specified against each grade of sealing compound.
1. MAK SEALING COMPOUND: GRADE A- IS 1834/1984.
It is an ideal hot pour Sealing Compound specially rubberised to withstand cracking besides having good adhesion to concrete it is also durable and is not affected by temperature changes. It has working temperature of 175???C - 185???C and a density of 1020 kg per cubic metre.
2. MAK SEALING COMPOUND: GRADE B - IS 1834/1984.
It is unaffected by petrol spillage especially jet fuel. It is therefore recommended for use in garages, filling stations etc., where there is spillage of petrol, oil and grease. It has a working temperature of 155???C- 165???C and a density of 1200 kg per cubic metre. On application of this product Mak Jet Primer is to be applied by brush or spray to ensure for proper adhesion. Care should be taken to see that Primer has sufficiently dried prior to pouring of Mak Sealing Compound into the Joint.
Usage of Sealing Compound and Primer:
1. MAK PRIMER: The consumption, for 25mm depth of joint would be one litre for 80 running metre length.
The quantity of Joint Sealing Compound required per 100 metre of running joint per 25mm depth with various thickness in kilos is indicated below:
9.5 mm thickness 35kg 12.0 mm thickness 48kg 18.0 mm thickness 70kg 25.0 mm thickness 95kg
Instructions for Sealing of Joints:
1. Every possible precaution should be taken to ensure that the joints are clean and free from debris and other foreign matter at the time of laying and during the curing process. 2. The primer is applied cold either by a spraying machine or by brush. Primers are inflammable and should not be placed near a named flame.
Construction and Contraction Joints:
In concrete pavements and runways, it is normal practice to provide butt joints with sealing groove 19mm in width at the top in order to facilitate the placing of the concrete.
Mak Sealing Compounds are available in 20kg, 25kg & 200kg capacity drums.
Mak Crete MWP is an acrylic based polymer modified cementitious water proofing system. The MAK CRETE polymer, when mixed with cement will provide the unique solution to all problems related to water leakage and protects from severe fungus, salt penetration, or environmental attack in the following structures:
• Roof Slab, Parapet, Terrace, Balconies. • Basements, Retaining Walls, tunnels, etc. • Bathroom and any floor to dampness • Against corrosion and salt attacks • Water Tanks or swimming pools • General concrete repair
When mix with the cement, it will provide better adhesive properties, impact resistance, flexural strength, and thin section fragility when compared with ordinary cement mortar.
• Mak Crete MWP increases the plasticity of concrete and cement. • Provided a tough and hard surface with water proofing. • Resistant to salt penetration • Resistant to UV rays, mild acids to strong alkalis. • Non-Flammable. • No health hazards to workmen. • Can be applied on horizontal as well as vertical surfaces.
HOW IT WORKS
It is well accepted fact that the damage skin or flesh of human body is only replaced with the skin or flesh of similar body. Likewise, damaged cementitious concrete or mortar should always be replaced by same kind of material. But cement particularly is having poor adhesive properties, low flexural and impact strength and mainly thin section fragility. Addition of acrylic polymer MAKCRETE into cement acts as a bonding agent and forms a hard, impermeable film which prevents not only water and fume but also allow the structure to breathe. This film, unlike all other existing conventional materials is flexible enough to take care of the thermal movement of structure and protects from severe attacks during all seasons.
The area to be coated must be sound clean, and free from oils, grease, or any other surface contaminants. Remove any loose material by scraping, chipping, mechanical abrasion, or any other suitable method. Visible cracks or any porous substrate are to be filled or levelled by using filler. The prepared surface is to be adequately saturated with water for atleast one hour before application, but leave no puddle of water. Cleaning of salt attacked area can be thoroughly washed muretic acid followed by copious water till neutral to litmus. Excellent surface preparation will ensure superior water proofing, excellent bonding & economic coverage.
Take 1 part by weight of MAK CRETE into a clean container and then add gradually 2 parts by weight of fresh cement under continuous mixing till a lump free pintable consistency is achieved. NEVER ADD LIQUID INTO THE CEMENT.
The slurry made by the above method is to be applied by a wide flat brush or broom across the prepared area uniformly. Apply the second coat of the freshly mixed slurry soon after the first coat is air dried sufficiently (Normally 3 to 6 hours). Stir frequently during use to offset settlement. NEVER USE A PREPARED SLURRY MORE THAN 30 MINUTES OLD.
MAK CRETE composite slurry system does not require continuous wet curing or ponding but it is recommended only after 24 hours of final coat application sprinkling of water or a cover with a plastic sheet to minimize.
??? Base: Emulsified Acrylic polymer ??? Appearance: White, Milky Liquid dries to colourless coating ??? Shelf Life: One year if unopened and stored properly. ??? Toxicity: Non toxic but avoid inhalation ??? Solid contents: >30% ??? Packing: 5 kg, 20 kg and 200 kg containers.
MAK POLYPLAST SUPERIOR is a polymeric waterproofing membrane consisting of five layers. The Centre core consists of 100 micron High Molecular High Density Polyethylene Film. The Polyethylene Film is the reinforcement barrier against water and moisture. The centre core is provided on both sides with SBS/APP polymer modified bitumen with properties of high Softening point, Heat resistance and High penetration making it ideal for waterproofing purposes.
Legal Status of FirmLimited Company (Ltd./Pvt.Ltd.)
Import Export Code (IEC)05950*****
Trust Seal Verified
Our three decades of industry experience assist us in fabricating a wide range of waterproofing membranes, waterproofing coatings, anti corrosive and reflective paints, anti corrosive pipeline coatings, road construction chemicals, joint sealing compounds. In addition, we have the sound infrastructure, facilities, and service of an experienced workforce to manufacture products as per the given specification of our clients. Makphalt products are known for the perfect mix of quality and pricing. “We aim to be an integral part of improving infrastructure construction in India.” We have our production facility as well as the corporate office located in the Delhi/NCR region where we efficiently run production operations and achieve the most competitive pricing for the entire product range. We have been doing application projects on a wide scale with most government departments (such as NTPC, CPWD, HAL, BCCL, NDMC and so on).